forked from materialsproject/pymatgen
-
Notifications
You must be signed in to change notification settings - Fork 0
/
Copy pathCod_2100513.cif
875 lines (869 loc) · 28.3 KB
/
Cod_2100513.cif
1
2
3
4
5
6
7
8
9
10
11
12
13
14
15
16
17
18
19
20
21
22
23
24
25
26
27
28
29
30
31
32
33
34
35
36
37
38
39
40
41
42
43
44
45
46
47
48
49
50
51
52
53
54
55
56
57
58
59
60
61
62
63
64
65
66
67
68
69
70
71
72
73
74
75
76
77
78
79
80
81
82
83
84
85
86
87
88
89
90
91
92
93
94
95
96
97
98
99
100
101
102
103
104
105
106
107
108
109
110
111
112
113
114
115
116
117
118
119
120
121
122
123
124
125
126
127
128
129
130
131
132
133
134
135
136
137
138
139
140
141
142
143
144
145
146
147
148
149
150
151
152
153
154
155
156
157
158
159
160
161
162
163
164
165
166
167
168
169
170
171
172
173
174
175
176
177
178
179
180
181
182
183
184
185
186
187
188
189
190
191
192
193
194
195
196
197
198
199
200
201
202
203
204
205
206
207
208
209
210
211
212
213
214
215
216
217
218
219
220
221
222
223
224
225
226
227
228
229
230
231
232
233
234
235
236
237
238
239
240
241
242
243
244
245
246
247
248
249
250
251
252
253
254
255
256
257
258
259
260
261
262
263
264
265
266
267
268
269
270
271
272
273
274
275
276
277
278
279
280
281
282
283
284
285
286
287
288
289
290
291
292
293
294
295
296
297
298
299
300
301
302
303
304
305
306
307
308
309
310
311
312
313
314
315
316
317
318
319
320
321
322
323
324
325
326
327
328
329
330
331
332
333
334
335
336
337
338
339
340
341
342
343
344
345
346
347
348
349
350
351
352
353
354
355
356
357
358
359
360
361
362
363
364
365
366
367
368
369
370
371
372
373
374
375
376
377
378
379
380
381
382
383
384
385
386
387
388
389
390
391
392
393
394
395
396
397
398
399
400
401
402
403
404
405
406
407
408
409
410
411
412
413
414
415
416
417
418
419
420
421
422
423
424
425
426
427
428
429
430
431
432
433
434
435
436
437
438
439
440
441
442
443
444
445
446
447
448
449
450
451
452
453
454
455
456
457
458
459
460
461
462
463
464
465
466
467
468
469
470
471
472
473
474
475
476
477
478
479
480
481
482
483
484
485
486
487
488
489
490
491
492
493
494
495
496
497
498
499
500
501
502
503
504
505
506
507
508
509
510
511
512
513
514
515
516
517
518
519
520
521
522
523
524
525
526
527
528
529
530
531
532
533
534
535
536
537
538
539
540
541
542
543
544
545
546
547
548
549
550
551
552
553
554
555
556
557
558
559
560
561
562
563
564
565
566
567
568
569
570
571
572
573
574
575
576
577
578
579
580
581
582
583
584
585
586
587
588
589
590
591
592
593
594
595
596
597
598
599
600
601
602
603
604
605
606
607
608
609
610
611
612
613
614
615
616
617
618
619
620
621
622
623
624
625
626
627
628
629
630
631
632
633
634
635
636
637
638
639
640
641
642
643
644
645
646
647
648
649
650
651
652
653
654
655
656
657
658
659
660
661
662
663
664
665
666
667
668
669
670
671
672
673
674
675
676
677
678
679
680
681
682
683
684
685
686
687
688
689
690
691
692
693
694
695
696
697
698
699
700
701
702
703
704
705
706
707
708
709
710
711
712
713
714
715
716
717
718
719
720
721
722
723
724
725
726
727
728
729
730
731
732
733
734
735
736
737
738
739
740
741
742
743
744
745
746
747
748
749
750
751
752
753
754
755
756
757
758
759
760
761
762
763
764
765
766
767
768
769
770
771
772
773
774
775
776
777
778
779
780
781
782
783
784
785
786
787
788
789
790
791
792
793
794
795
796
797
798
799
800
801
802
803
804
805
806
807
808
809
810
811
812
813
814
815
816
817
818
819
820
821
822
823
824
825
826
827
828
829
830
831
832
833
834
835
836
837
838
839
840
841
842
843
844
845
846
847
848
849
850
851
852
853
854
855
856
857
858
859
860
861
862
863
864
865
866
867
868
869
870
871
872
873
874
875
#------------------------------------------------------------------------------
#$Date: 2016-02-20 01:53:41 +0100 (Sat, 20 Feb 2016) $
#$Revision: 176768 $
#$URL: svn://www.crystallography.net/cod/cif/2/10/05/2100513.cif $
#------------------------------------------------------------------------------
#
# This file is available in the Crystallography Open Database (COD),
# http://www.crystallography.net/. The original data for this entry
# were provided by IUCr Journals, http://journals.iucr.org/.
#
# The file may be used within the scientific community so long as
# proper attribution is given to the journal article from which the
# data were obtained.
#
data_2100513
loop_
_publ_author_name
'Barnes, Paris W.'
'Lufaso, Michael W.'
'Woodward, Patrick M.'
_publ_section_title
;
Structure determination of <i>A</i>~2~<i>M</i>^3+^TaO~6~ and
<i>A</i>~2~<i>M</i>^3+^NbO~6~ ordered perovskites: octahedral tilting
and pseudosymmetry
;
_journal_coeditor_code WS5031
_journal_date_accepted 2006-01-19
_journal_date_recd_electronic 2005-06-10
_journal_issue 3
_journal_name_full 'Acta Crystallographica Section B'
_journal_page_first 384
_journal_page_last 396
_journal_paper_category FA
_journal_paper_doi 10.1107/S0108768106002448
_journal_volume 62
_journal_year 2006
_chemical_formula_sum 'Al Ca2 Nb O6'
_chemical_formula_weight 296.04
_space_group_IT_number 14
_symmetry_cell_setting monoclinic
_symmetry_space_group_name_Hall '-P 2yn'
_symmetry_space_group_name_H-M 'P 1 21/n 1'
_audit_creation_method 'from EXP file using GSAS2CIF'
_cell_angle_alpha 90.0
_cell_angle_beta 89.970(4)
_cell_angle_gamma 90.0
_cell_formula_units_Z 2
_cell_length_a 5.37706(9)
_cell_length_b 5.41557(9)
_cell_length_c 7.62550(13)
_cell_measurement_temperature 298
_cell_volume 222.053(6)
_computing_structure_refinement GSAS
_diffrn_ambient_temperature 298
_diffrn_measurement_device BT-1
_diffrn_measurement_method reactor
_diffrn_radiation_probe neutron
_diffrn_radiation_source NIST
_diffrn_radiation_type neutron
_diffrn_radiation_wavelength 1.5403
_exptl_crystal_density_diffrn 4.428
_refine_ls_goodness_of_fit_all 1.22
_refine_ls_matrix_type full
_refine_ls_number_parameters 43
_refine_ls_number_restraints 0
_refine_ls_shift/su_max 0.02
_refine_ls_shift/su_mean 0.01
_cod_data_source_file ws5031.cif
_cod_data_source_block Ca2AlNbO6
_cod_depositor_comments
;
The following automatic conversions were performed:
'_geom_bond_publ_flag' value 'N' changed to 'n' according to
'/home/saulius/struct/CIF-dictionaries/cif_core.dic' dictionary named
'cif_core.dic' version 2.4.1 from 2010-06-29 (114
times).
'_geom_angle_publ_flag' value 'N' changed to 'n' according to
'/home/saulius/struct/CIF-dictionaries/cif_core.dic' dictionary named
'cif_core.dic' version 2.4.1 from 2010-06-29 (615 times).
Automatic conversion script
Id: cif_fix_enum 1527 2010-12-29 10:47:43Z saulius
The following automatic conversions were performed:
'_geom_bond_publ_flag' value 'N' changed to 'n' according to
/home/saulius/struct/CIF-dictionaries/cif_core.dic dictionary named
'cif_core.dic' version 2.4.1 from 2010-06-29 (114
times).
'_geom_angle_publ_flag' value 'N' changed to 'n' according
to /home/saulius/struct/CIF-dictionaries/cif_core.dic dictionary
named 'cif_core.dic' version 2.4.1 from 2010-06-29 (615 times).
Automatic conversion script
Id: cif_fix_values 1715 2011-07-08 13:25:40Z adriana
;
_cod_original_cell_volume 222.050(10)
_cod_original_sg_symbol_H-M P21/n
_cod_database_code 2100513
loop_
_symmetry_equiv_pos_site_id
_symmetry_equiv_pos_as_xyz
1 +x,+y,+z
2 -x+1/2,+y+1/2,-z+1/2
-1 -x,-y,-z
-2 +x+1/2,-y+1/2,+z+1/2
loop_
_atom_site_type_symbol
_atom_site_label
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
_atom_site_U_iso_or_equiv
_atom_site_thermal_displace_type
_atom_site_occupancy
CA Ca 0.5059(4) 0.5309(2) 0.2485(8) 0.0116(3) Uiso 1.0
AL Al1 0.0 0.5 0.0 0.00365(19) Uiso 0.941(8)
NB Nb1 0.0 0.5 0.0 0.00365(19) Uiso 0.059(8)
AL Al2 0.5 0.0 0.0 0.00365(19) Uiso 0.059(8)
NB Nb2 0.5 0.0 0.0 0.00365(19) Uiso 0.941(8)
O O1 0.2092(6) 0.2158(7) -0.0340(5) 0.0063(8) Uiso 1.0
O O2 0.2824(6) 0.7130(8) -0.0338(6) 0.0091(8) Uiso 1.0
O O3 0.4333(2) -0.01305(19) 0.2529(6) 0.0085(3) Uiso 1.0
loop_
_atom_type_symbol
Ca
Al
Nb
O
loop_
_geom_angle_atom_site_label_1
_geom_angle_atom_site_label_2
_geom_angle_atom_site_label_3
_geom_angle_site_symmetry_1
_geom_angle_site_symmetry_3
_geom_angle
_geom_angle_publ_flag
Ca Ca Ca 2_545 2_555 89.08(9) n
Ca Ca Ca 2_545 2_645 89.573(4) n
Ca Ca Ca 2_545 2_655 178.49(19) n
Ca Ca Ca 2_545 -1_665 86.11(17) n
Ca Ca Ca 2_545 -1_666 85.51(18) n
Ca Ca Al1 2_545 1_555 51.97(9) n
Ca Ca Al1 2_545 1_655 123.17(17) n
Ca Ca Al1 2_545 2_555 123.32(19) n
Ca Ca Nb1 2_545 1_555 51.97(9) n
Ca Ca Nb1 2_545 1_655 123.17(17) n
Ca Ca Nb1 2_545 2_555 123.32(19) n
Ca Ca Al2 2_545 1_565 123.96(18) n
Ca Ca Al2 2_545 2_555 51.65(10) n
Ca Ca Al2 2_545 2_655 122.54(16) n
Ca Ca Nb2 2_545 1_565 123.96(18) n
Ca Ca Nb2 2_545 2_555 51.65(10) n
Ca Ca Nb2 2_545 2_655 122.54(16) n
Ca Ca O1 2_545 2_555 87.10(17) n
Ca Ca O1 2_545 -1_665 141.8(3) n
Ca Ca O1 2_545 -2_666 86.00(14) n
Ca Ca O2 2_545 1_555 86.71(17) n
Ca Ca O2 2_545 -1_665 87.47(14) n
Ca Ca O2 2_545 -2_676 140.4(3) n
Ca Ca O3 2_545 1_565 125.55(10) n
Ca Ca Ca 2_555 2_645 178.49(19) n
Ca Ca Ca 2_555 2_655 89.573(4) n
Ca Ca Ca 2_555 -1_665 93.19(19) n
Ca Ca Ca 2_555 -1_666 92.5(2) n
Ca Ca Al1 2_555 1_555 56.95(9) n
Ca Ca Al1 2_555 1_655 128.24(18) n
Ca Ca Al1 2_555 2_555 55.23(9) n
Ca Ca Nb1 2_555 1_555 56.95(9) n
Ca Ca Nb1 2_555 1_655 128.24(18) n
Ca Ca Nb1 2_555 2_555 55.23(9) n
Ca Ca Al2 2_555 1_565 55.54(8) n
Ca Ca Al2 2_555 2_555 56.64(10) n
Ca Ca Al2 2_555 2_655 127.55(18) n
Ca Ca Nb2 2_555 1_565 55.54(8) n
Ca Ca Nb2 2_555 2_555 56.64(10) n
Ca Ca Nb2 2_555 2_655 127.55(18) n
Ca Ca O1 2_555 2_555 54.66(14) n
Ca Ca O1 2_555 -1_665 93.04(13) n
Ca Ca O1 2_555 -2_666 135.5(3) n
Ca Ca O2 2_555 1_555 54.66(14) n
Ca Ca O2 2_555 -1_665 136.9(3) n
Ca Ca O2 2_555 -2_676 91.69(14) n
Ca Ca O3 2_555 1_565 36.48(3) n
Ca Ca Ca 2_645 2_655 91.76(9) n
Ca Ca Ca 2_645 -1_665 87.42(18) n
Ca Ca Ca 2_645 -1_666 86.70(17) n
Ca Ca Al1 2_645 1_555 122.54(16) n
Ca Ca Al1 2_645 1_655 53.19(10) n
Ca Ca Al1 2_645 2_555 125.16(19) n
Ca Ca Nb1 2_645 1_555 122.54(16) n
Ca Ca Nb1 2_645 1_655 53.19(10) n
Ca Ca Nb1 2_645 2_555 125.16(19) n
Ca Ca Al2 2_645 1_565 125.9(2) n
Ca Ca Al2 2_645 2_555 121.90(17) n
Ca Ca Al2 2_645 2_655 52.84(9) n
Ca Ca Nb2 2_645 1_565 125.9(2) n
Ca Ca Nb2 2_645 2_555 121.90(17) n
Ca Ca Nb2 2_645 2_655 52.84(9) n
Ca Ca O1 2_645 2_555 124.6(3) n
Ca Ca O1 2_645 -1_665 88.45(15) n
Ca Ca O1 2_645 -2_666 43.70(13) n
Ca Ca O2 2_645 1_555 125.9(3) n
Ca Ca O2 2_645 -1_665 43.66(13) n
Ca Ca O2 2_645 -2_676 88.90(15) n
Ca Ca O3 2_645 1_565 144.85(10) n
Ca Ca Ca 2_655 -1_665 94.7(2) n
Ca Ca Ca 2_655 -1_666 93.9(2) n
Ca Ca Al1 2_655 1_555 127.61(18) n
Ca Ca Al1 2_655 1_655 58.29(10) n
Ca Ca Al1 2_655 2_555 55.25(9) n
Ca Ca Nb1 2_655 1_555 127.61(18) n
Ca Ca Nb1 2_655 1_655 58.29(10) n
Ca Ca Nb1 2_655 2_555 55.25(9) n
Ca Ca Al2 2_655 1_565 55.63(9) n
Ca Ca Al2 2_655 2_555 126.91(18) n
Ca Ca Al2 2_655 2_655 57.94(10) n
Ca Ca Nb2 2_655 1_565 55.63(9) n
Ca Ca Nb2 2_655 2_555 126.91(18) n
Ca Ca Nb2 2_655 2_655 57.94(10) n
Ca Ca O1 2_655 2_555 91.55(17) n
Ca Ca O1 2_655 -1_665 39.04(12) n
Ca Ca O1 2_655 -2_666 94.48(17) n
Ca Ca O2 2_655 1_555 93.08(17) n
Ca Ca O2 2_655 -1_665 93.99(18) n
Ca Ca O2 2_655 -2_676 38.96(13) n
Ca Ca O3 2_655 1_565 53.10(3) n
Ca Ca Ca -1_665 -1_666 169.79(7) n
Ca Ca Al1 -1_665 1_555 54.07(9) n
Ca Ca Al1 -1_665 1_655 55.37(10) n
Ca Ca Al1 -1_665 2_555 132.08(11) n
Ca Ca Nb1 -1_665 1_555 54.07(9) n
Ca Ca Nb1 -1_665 1_655 55.37(10) n
Ca Ca Nb1 -1_665 2_555 132.08(11) n
Ca Ca Al2 -1_665 1_565 58.33(10) n
Ca Ca Al2 -1_665 2_555 123.71(11) n
Ca Ca Al2 -1_665 2_655 126.26(13) n
Ca Ca Nb2 -1_665 1_565 58.33(10) n
Ca Ca Nb2 -1_665 2_555 123.71(11) n
Ca Ca Nb2 -1_665 2_655 126.26(13) n
Ca Ca O1 -1_665 2_555 147.23(14) n
Ca Ca O1 -1_665 -1_665 55.66(15) n
Ca Ca O1 -1_665 -2_666 130.44(15) n
Ca Ca O2 -1_665 1_555 38.53(13) n
Ca Ca O2 -1_665 -1_665 43.75(14) n
Ca Ca O2 -1_665 -2_676 133.32(18) n
Ca Ca O3 -1_665 1_565 95.6(2) n
Ca Ca Al1 -1_666 1_555 123.44(12) n
Ca Ca Al1 -1_666 1_655 125.88(12) n
Ca Ca Al1 -1_666 2_555 57.93(10) n
Ca Ca Nb1 -1_666 1_555 123.44(12) n
Ca Ca Nb1 -1_666 1_655 125.88(12) n
Ca Ca Nb1 -1_666 2_555 57.93(10) n
Ca Ca Al2 -1_666 1_565 131.68(11) n
Ca Ca Al2 -1_666 2_555 53.79(10) n
Ca Ca Al2 -1_666 2_655 54.99(9) n
Ca Ca Nb2 -1_666 1_565 131.68(11) n
Ca Ca Nb2 -1_666 2_555 53.79(10) n
Ca Ca Nb2 -1_666 2_655 54.99(9) n
Ca Ca O1 -1_666 2_555 37.88(12) n
Ca Ca O1 -1_666 -1_665 132.43(16) n
Ca Ca O1 -1_666 -2_666 43.00(13) n
Ca Ca O2 -1_666 1_555 146.35(16) n
Ca Ca O2 -1_666 -1_665 129.90(15) n
Ca Ca O2 -1_666 -2_676 54.89(15) n
Ca Ca O3 -1_666 1_565 94.00(19) n
Al1 Ca Al1 1_555 1_655 109.44(17) n
Al1 Ca Al1 1_555 2_555 112.10(5) n
Al1 Ca Nb1 1_555 1_555 0.0 n
Al1 Ca Nb1 1_555 1_655 109.44(17) n
Al1 Ca Nb1 1_555 2_555 112.10(5) n
Al1 Ca Al2 1_555 1_565 71.99(9) n
Al1 Ca Al2 1_555 2_555 69.95(4) n
Al1 Ca Al2 1_555 2_655 174.11(5) n
Al1 Ca Nb2 1_555 1_565 71.99(9) n
Al1 Ca Nb2 1_555 2_555 69.95(4) n
Al1 Ca Nb2 1_555 2_655 174.11(5) n
Al1 Ca O1 1_555 2_555 97.48(10) n
Al1 Ca O1 1_555 -1_665 98.56(18) n
Al1 Ca O1 1_555 -2_666 137.88(10) n
Al1 Ca O2 1_555 1_555 35.40(9) n
Al1 Ca O2 1_555 -1_665 88.36(16) n
Al1 Ca O2 1_555 -2_676 148.43(10) n
Al1 Ca O3 1_555 1_565 85.96(12) n
Al1 Ca Al1 1_655 2_555 113.46(5) n
Al1 Ca Nb1 1_655 1_555 109.44(17) n
Al1 Ca Nb1 1_655 1_655 0.0 n
Al1 Ca Nb1 1_655 2_555 113.46(5) n
Al1 Ca Al2 1_655 1_565 72.70(10) n
Al1 Ca Al2 1_655 2_555 174.17(4) n
Al1 Ca Al2 1_655 2_655 71.21(4) n
Al1 Ca Nb2 1_655 1_565 72.70(10) n
Al1 Ca Nb2 1_655 2_555 174.17(4) n
Al1 Ca Nb2 1_655 2_655 71.21(4) n
Al1 Ca O1 1_655 2_555 147.89(12) n
Al1 Ca O1 1_655 -1_665 36.08(9) n
Al1 Ca O1 1_655 -2_666 90.09(11) n
Al1 Ca O2 1_655 1_555 85.25(17) n
Al1 Ca O2 1_655 -1_665 35.69(9) n
Al1 Ca O2 1_655 -2_676 86.17(11) n
Al1 Ca O3 1_655 1_565 100.69(12) n
Al1 Ca Nb1 2_555 1_555 112.10(5) n
Al1 Ca Nb1 2_555 1_655 113.46(5) n
Al1 Ca Nb1 2_555 2_555 0.0 n
Al1 Ca Al2 2_555 1_565 73.77(2) n
Al1 Ca Al2 2_555 2_555 71.66(10) n
Al1 Ca Al2 2_555 2_655 72.32(9) n
Al1 Ca Nb2 2_555 1_565 73.77(2) n
Al1 Ca Nb2 2_555 2_555 71.66(10) n
Al1 Ca Nb2 2_555 2_655 72.32(9) n
Al1 Ca O1 2_555 2_555 37.10(9) n
Al1 Ca O1 2_555 -1_665 87.94(9) n
Al1 Ca O1 2_555 -2_666 91.84(19) n
Al1 Ca O2 2_555 1_555 100.82(10) n
Al1 Ca O2 2_555 -1_665 149.07(11) n
Al1 Ca O2 2_555 -2_676 37.14(9) n
Al1 Ca O3 2_555 1_565 37.07(12) n
Nb1 Ca Nb1 1_555 1_655 109.44(17) n
Nb1 Ca Nb1 1_555 2_555 112.10(5) n
Nb1 Ca Al2 1_555 1_565 71.99(9) n
Nb1 Ca Al2 1_555 2_555 69.95(4) n
Nb1 Ca Al2 1_555 2_655 174.11(5) n
Nb1 Ca Nb2 1_555 1_565 71.99(9) n
Nb1 Ca Nb2 1_555 2_555 69.95(4) n
Nb1 Ca Nb2 1_555 2_655 174.11(5) n
Nb1 Ca O1 1_555 2_555 97.48(10) n
Nb1 Ca O1 1_555 -1_665 98.56(18) n
Nb1 Ca O1 1_555 -2_666 137.88(10) n
Nb1 Ca O2 1_555 1_555 35.40(9) n
Nb1 Ca O2 1_555 -1_665 88.36(16) n
Nb1 Ca O2 1_555 -2_676 148.43(10) n
Nb1 Ca O3 1_555 1_565 85.96(12) n
Nb1 Ca Nb1 1_655 2_555 113.46(5) n
Nb1 Ca Al2 1_655 1_565 72.70(10) n
Nb1 Ca Al2 1_655 2_555 174.17(4) n
Nb1 Ca Al2 1_655 2_655 71.21(4) n
Nb1 Ca Nb2 1_655 1_565 72.70(10) n
Nb1 Ca Nb2 1_655 2_555 174.17(4) n
Nb1 Ca Nb2 1_655 2_655 71.21(4) n
Nb1 Ca O1 1_655 2_555 147.89(12) n
Nb1 Ca O1 1_655 -1_665 36.08(9) n
Nb1 Ca O1 1_655 -2_666 90.09(11) n
Nb1 Ca O2 1_655 1_555 85.25(17) n
Nb1 Ca O2 1_655 -1_665 35.69(9) n
Nb1 Ca O2 1_655 -2_676 86.17(11) n
Nb1 Ca O3 1_655 1_565 100.69(12) n
Nb1 Ca Al2 2_555 1_565 73.77(2) n
Nb1 Ca Al2 2_555 2_555 71.66(10) n
Nb1 Ca Al2 2_555 2_655 72.32(9) n
Nb1 Ca Nb2 2_555 1_565 73.77(2) n
Nb1 Ca Nb2 2_555 2_555 71.66(10) n
Nb1 Ca Nb2 2_555 2_655 72.32(9) n
Nb1 Ca O1 2_555 2_555 37.10(9) n
Nb1 Ca O1 2_555 -1_665 87.94(9) n
Nb1 Ca O1 2_555 -2_666 91.84(19) n
Nb1 Ca O2 2_555 1_555 100.82(10) n
Nb1 Ca O2 2_555 -1_665 149.07(11) n
Nb1 Ca O2 2_555 -2_676 37.14(9) n
Nb1 Ca O3 2_555 1_565 37.07(12) n
Al2 Ca Al2 1_565 2_555 112.09(5) n
Al2 Ca Al2 1_565 2_655 113.49(5) n
Al2 Ca Nb2 1_565 1_565 0.0 n
Al2 Ca Nb2 1_565 2_555 112.09(5) n
Al2 Ca Nb2 1_565 2_655 113.49(5) n
Al2 Ca O1 1_565 2_555 100.55(10) n
Al2 Ca O1 1_565 -1_665 38.30(9) n
Al2 Ca O1 1_565 -2_666 150.00(12) n
Al2 Ca O2 1_565 1_555 38.11(9) n
Al2 Ca O2 1_565 -1_665 92.2(2) n
Al2 Ca O2 1_565 -2_676 87.74(10) n
Al2 Ca O3 1_565 1_565 38.27(12) n
Al2 Ca Al2 2_555 2_655 108.78(17) n
Al2 Ca Nb2 2_555 1_565 112.09(5) n
Al2 Ca Nb2 2_555 2_555 0.0 n
Al2 Ca Nb2 2_555 2_655 108.78(17) n
Al2 Ca O1 2_555 2_555 36.23(8) n
Al2 Ca O1 2_555 -1_665 149.36(8) n
Al2 Ca O1 2_555 -2_666 86.91(16) n
Al2 Ca O2 2_555 1_555 96.64(11) n
Al2 Ca O2 2_555 -1_665 138.99(10) n
Al2 Ca O2 2_555 -2_676 97.17(19) n
Al2 Ca O3 2_555 1_565 85.09(11) n
Al2 Ca Nb2 2_655 1_565 113.49(5) n
Al2 Ca Nb2 2_655 2_555 108.78(17) n
Al2 Ca Nb2 2_655 2_655 0.0 n
Al2 Ca O1 2_655 2_555 83.84(16) n
Al2 Ca O1 2_655 -1_665 85.32(10) n
Al2 Ca O1 2_655 -2_666 36.54(10) n
Al2 Ca O2 2_655 1_555 149.26(13) n
Al2 Ca O2 2_655 -1_665 89.23(9) n
Al2 Ca O2 2_655 -2_676 36.72(9) n
Al2 Ca O3 2_655 1_565 99.72(13) n
Nb2 Ca Nb2 1_565 2_555 112.09(5) n
Nb2 Ca Nb2 1_565 2_655 113.49(5) n
Nb2 Ca O1 1_565 2_555 100.55(10) n
Nb2 Ca O1 1_565 -1_665 38.30(9) n
Nb2 Ca O1 1_565 -2_666 150.00(12) n
Nb2 Ca O2 1_565 1_555 38.11(9) n
Nb2 Ca O2 1_565 -1_665 92.2(2) n
Nb2 Ca O2 1_565 -2_676 87.74(10) n
Nb2 Ca O3 1_565 1_565 38.27(12) n
Nb2 Ca Nb2 2_555 2_655 108.78(17) n
Nb2 Ca O1 2_555 2_555 36.23(8) n
Nb2 Ca O1 2_555 -1_665 149.36(8) n
Nb2 Ca O1 2_555 -2_666 86.91(16) n
Nb2 Ca O2 2_555 1_555 96.64(11) n
Nb2 Ca O2 2_555 -1_665 138.99(10) n
Nb2 Ca O2 2_555 -2_676 97.17(19) n
Nb2 Ca O3 2_555 1_565 85.09(11) n
Nb2 Ca O1 2_655 2_555 83.84(16) n
Nb2 Ca O1 2_655 -1_665 85.32(10) n
Nb2 Ca O1 2_655 -2_666 36.54(10) n
Nb2 Ca O2 2_655 1_555 149.26(13) n
Nb2 Ca O2 2_655 -1_665 89.23(9) n
Nb2 Ca O2 2_655 -2_676 36.72(9) n
Nb2 Ca O3 2_655 1_565 99.72(13) n
O1 Ca O1 2_555 -1_665 124.48(8) n
O1 Ca O1 2_555 -2_666 80.9(2) n
O1 Ca O2 2_555 1_555 109.08(7) n
O1 Ca O2 2_555 -1_665 167.1(2) n
O1 Ca O2 2_555 -2_676 61.94(18) n
O1 Ca O3 2_555 1_565 63.22(13) n
O1 Ca O1 -1_665 -2_666 117.14(12) n
O1 Ca O2 -1_665 1_555 64.25(19) n
O1 Ca O2 -1_665 -1_665 65.5(2) n
O1 Ca O2 -1_665 -2_676 77.74(6) n
O1 Ca O3 -1_665 1_565 65.40(10) n
O1 Ca O2 -2_666 1_555 167.3(2) n
O1 Ca O2 -2_666 -1_665 87.06(7) n
O1 Ca O2 -2_666 -2_676 66.3(2) n
O1 Ca O3 -2_666 1_565 127.8(3) n
O2 Ca O2 1_555 -1_665 82.3(2) n
O2 Ca O2 1_555 -2_676 124.97(7) n
O2 Ca O3 1_555 1_565 64.76(13) n
O2 Ca O2 -1_665 -2_676 117.07(11) n
O2 Ca O3 -1_665 1_565 129.0(3) n
O2 Ca O3 -2_676 1_565 63.78(10) n
Ca Al1 Ca 1_455 1_555 109.44(17) n
Ca Al1 Ca 1_455 2_545 71.56(4) n
Ca Al1 Ca 1_455 -1_565 70.56(17) n
Ca Al1 Ca 1_455 -1_665 180.0 n
Ca Al1 Ca 1_455 -2_575 108.44(4) n
Ca Al1 O1 1_455 1_555 126.48(12) n
Ca Al1 O1 1_455 -1_565 53.52(12) n
Ca Al1 O2 1_455 1_555 133.51(14) n
Ca Al1 O2 1_455 -1_565 46.49(14) n
Ca Al1 O3 1_455 2_555 65.49(10) n
Ca Al1 O3 1_455 -2_565 114.51(10) n
Ca Al1 Ca 1_555 2_545 72.79(4) n
Ca Al1 Ca 1_555 -1_565 179.972 n
Ca Al1 Ca 1_555 -1_665 70.56(17) n
Ca Al1 Ca 1_555 -2_575 107.21(4) n
Ca Al1 O1 1_555 1_555 68.78(13) n
Ca Al1 O1 1_555 -1_565 111.22(13) n
Ca Al1 O2 1_555 1_555 53.08(14) n
Ca Al1 O2 1_555 -1_565 126.92(14) n
Ca Al1 O3 1_555 2_555 44.60(10) n
Ca Al1 O3 1_555 -2_565 135.40(10) n
Ca Al1 Ca 2_545 -1_565 107.21(4) n
Ca Al1 Ca 2_545 -1_665 108.44(4) n
Ca Al1 Ca 2_545 -2_575 179.9657 n
Ca Al1 O1 2_545 1_555 56.52(14) n
Ca Al1 O1 2_545 -1_565 123.48(14) n
Ca Al1 O2 2_545 1_555 124.51(13) n
Ca Al1 O2 2_545 -1_565 55.49(13) n
Ca Al1 O3 2_545 2_555 51.75(9) n
Ca Al1 O3 2_545 -2_565 128.25(9) n
Ca Al1 Ca -1_565 -1_665 109.44(17) n
Ca Al1 Ca -1_565 -2_575 72.79(4) n
Ca Al1 O1 -1_565 1_555 111.22(13) n
Ca Al1 O1 -1_565 -1_565 68.78(13) n
Ca Al1 O2 -1_565 1_555 126.92(14) n
Ca Al1 O2 -1_565 -1_565 53.08(14) n
Ca Al1 O3 -1_565 2_555 135.40(10) n
Ca Al1 O3 -1_565 -2_565 44.60(10) n
Ca Al1 Ca -1_665 -2_575 71.56(4) n
Ca Al1 O1 -1_665 1_555 53.52(12) n
Ca Al1 O1 -1_665 -1_565 126.48(12) n
Ca Al1 O2 -1_665 1_555 46.49(14) n
Ca Al1 O2 -1_665 -1_565 133.51(14) n
Ca Al1 O3 -1_665 2_555 114.51(10) n
Ca Al1 O3 -1_665 -2_565 65.49(10) n
Ca Al1 O1 -2_575 1_555 123.48(14) n
Ca Al1 O1 -2_575 -1_565 56.52(14) n
Ca Al1 O2 -2_575 1_555 55.49(13) n
Ca Al1 O2 -2_575 -1_565 124.51(13) n
Ca Al1 O3 -2_575 2_555 128.25(9) n
Ca Al1 O3 -2_575 -2_565 51.75(9) n
O1 Al1 O1 1_555 -1_565 179.972 n
O1 Al1 O2 1_555 1_555 90.0(2) n
O1 Al1 O2 1_555 -1_565 90.0(2) n
O1 Al1 O3 1_555 2_555 89.61(14) n
O1 Al1 O3 1_555 -2_565 90.39(14) n
O1 Al1 O2 -1_565 1_555 90.0(2) n
O1 Al1 O2 -1_565 -1_565 90.0(2) n
O1 Al1 O3 -1_565 2_555 90.39(14) n
O1 Al1 O3 -1_565 -2_565 89.61(14) n
O2 Al1 O2 1_555 -1_565 180.0 n
O2 Al1 O3 1_555 2_555 90.31(14) n
O2 Al1 O3 1_555 -2_565 89.69(14) n
O2 Al1 O3 -1_565 2_555 89.69(14) n
O2 Al1 O3 -1_565 -2_565 90.31(14) n
O3 Al1 O3 2_555 -2_565 179.9802 n
Ca Nb1 Ca 1_455 1_555 109.44(17) n
Ca Nb1 Ca 1_455 2_545 71.56(4) n
Ca Nb1 Ca 1_455 -1_565 70.56(17) n
Ca Nb1 Ca 1_455 -1_665 180.0 n
Ca Nb1 Ca 1_455 -2_575 108.44(4) n
Ca Nb1 O1 1_455 1_555 126.48(12) n
Ca Nb1 O1 1_455 -1_565 53.52(12) n
Ca Nb1 O2 1_455 1_555 133.51(14) n
Ca Nb1 O2 1_455 -1_565 46.49(14) n
Ca Nb1 O3 1_455 2_555 65.49(10) n
Ca Nb1 O3 1_455 -2_565 114.51(10) n
Ca Nb1 Ca 1_555 2_545 72.79(4) n
Ca Nb1 Ca 1_555 -1_565 179.972 n
Ca Nb1 Ca 1_555 -1_665 70.56(17) n
Ca Nb1 Ca 1_555 -2_575 107.21(4) n
Ca Nb1 O1 1_555 1_555 68.78(13) n
Ca Nb1 O1 1_555 -1_565 111.22(13) n
Ca Nb1 O2 1_555 1_555 53.08(14) n
Ca Nb1 O2 1_555 -1_565 126.92(14) n
Ca Nb1 O3 1_555 2_555 44.60(10) n
Ca Nb1 O3 1_555 -2_565 135.40(10) n
Ca Nb1 Ca 2_545 -1_565 107.21(4) n
Ca Nb1 Ca 2_545 -1_665 108.44(4) n
Ca Nb1 Ca 2_545 -2_575 179.9657 n
Ca Nb1 O1 2_545 1_555 56.52(14) n
Ca Nb1 O1 2_545 -1_565 123.48(14) n
Ca Nb1 O2 2_545 1_555 124.51(13) n
Ca Nb1 O2 2_545 -1_565 55.49(13) n
Ca Nb1 O3 2_545 2_555 51.75(9) n
Ca Nb1 O3 2_545 -2_565 128.25(9) n
Ca Nb1 Ca -1_565 -1_665 109.44(17) n
Ca Nb1 Ca -1_565 -2_575 72.79(4) n
Ca Nb1 O1 -1_565 1_555 111.22(13) n
Ca Nb1 O1 -1_565 -1_565 68.78(13) n
Ca Nb1 O2 -1_565 1_555 126.92(14) n
Ca Nb1 O2 -1_565 -1_565 53.08(14) n
Ca Nb1 O3 -1_565 2_555 135.40(10) n
Ca Nb1 O3 -1_565 -2_565 44.60(10) n
Ca Nb1 Ca -1_665 -2_575 71.56(4) n
Ca Nb1 O1 -1_665 1_555 53.52(12) n
Ca Nb1 O1 -1_665 -1_565 126.48(12) n
Ca Nb1 O2 -1_665 1_555 46.49(14) n
Ca Nb1 O2 -1_665 -1_565 133.51(14) n
Ca Nb1 O3 -1_665 2_555 114.51(10) n
Ca Nb1 O3 -1_665 -2_565 65.49(10) n
Ca Nb1 O1 -2_575 1_555 123.48(14) n
Ca Nb1 O1 -2_575 -1_565 56.52(14) n
Ca Nb1 O2 -2_575 1_555 55.49(13) n
Ca Nb1 O2 -2_575 -1_565 124.51(13) n
Ca Nb1 O3 -2_575 2_555 128.25(9) n
Ca Nb1 O3 -2_575 -2_565 51.75(9) n
O1 Nb1 O1 1_555 -1_565 179.972 n
O1 Nb1 O2 1_555 1_555 90.0(2) n
O1 Nb1 O2 1_555 -1_565 90.0(2) n
O1 Nb1 O3 1_555 2_555 89.61(14) n
O1 Nb1 O3 1_555 -2_565 90.39(14) n
O1 Nb1 O2 -1_565 1_555 90.0(2) n
O1 Nb1 O2 -1_565 -1_565 90.0(2) n
O1 Nb1 O3 -1_565 2_555 90.39(14) n
O1 Nb1 O3 -1_565 -2_565 89.61(14) n
O2 Nb1 O2 1_555 -1_565 180.0 n
O2 Nb1 O3 1_555 2_555 90.31(14) n
O2 Nb1 O3 1_555 -2_565 89.69(14) n
O2 Nb1 O3 -1_565 2_555 89.69(14) n
O2 Nb1 O3 -1_565 -2_565 90.31(14) n
O3 Nb1 O3 2_555 -2_565 179.9802 n
Ca Al2 Ca 1_545 2_545 72.81(4) n
Ca Al2 Ca 1_545 2_645 71.53(4) n
Ca Al2 Ca 1_545 -1_665 179.9802 n
Ca Al2 Ca 1_545 -2_565 108.47(4) n
Ca Al2 Ca 1_545 -2_665 107.19(4) n
Ca Al2 O1 1_545 1_555 124.23(13) n
Ca Al2 O1 1_545 -1_655 55.77(13) n
Ca Al2 O2 1_545 1_545 56.61(14) n
Ca Al2 O2 1_545 -1_665 123.39(14) n
Ca Al2 O3 1_545 1_555 52.09(9) n
Ca Al2 O3 1_545 -1_655 127.91(9) n
Ca Al2 Ca 2_545 2_645 108.78(17) n
Ca Al2 Ca 2_545 -1_665 107.19(4) n
Ca Al2 Ca 2_545 -2_565 71.22(17) n
Ca Al2 Ca 2_545 -2_665 180.0 n
Ca Al2 O1 2_545 1_555 52.98(14) n
Ca Al2 O1 2_545 -1_655 127.02(14) n
Ca Al2 O2 2_545 1_545 68.20(13) n
Ca Al2 O2 2_545 -1_665 111.80(13) n
Ca Al2 O3 2_545 1_555 44.55(9) n
Ca Al2 O3 2_545 -1_655 135.45(9) n
Ca Al2 Ca 2_645 -1_665 108.47(4) n
Ca Al2 Ca 2_645 -2_565 179.972 n
Ca Al2 Ca 2_645 -2_665 71.22(17) n
Ca Al2 O1 2_645 1_555 133.61(13) n
Ca Al2 O1 2_645 -1_655 46.39(13) n
Ca Al2 O2 2_645 1_545 126.87(13) n
Ca Al2 O2 2_645 -1_665 53.13(13) n
Ca Al2 O3 2_645 1_555 64.87(10) n
Ca Al2 O3 2_645 -1_655 115.13(10) n
Ca Al2 Ca -1_665 -2_565 71.53(4) n
Ca Al2 Ca -1_665 -2_665 72.81(4) n
Ca Al2 O1 -1_665 1_555 55.77(13) n
Ca Al2 O1 -1_665 -1_655 124.23(13) n
Ca Al2 O2 -1_665 1_545 123.39(14) n
Ca Al2 O2 -1_665 -1_665 56.61(14) n
Ca Al2 O3 -1_665 1_555 127.91(9) n
Ca Al2 O3 -1_665 -1_655 52.09(9) n
Ca Al2 Ca -2_565 -2_665 108.78(17) n
Ca Al2 O1 -2_565 1_555 46.39(13) n
Ca Al2 O1 -2_565 -1_655 133.61(13) n
Ca Al2 O2 -2_565 1_545 53.13(13) n
Ca Al2 O2 -2_565 -1_665 126.87(13) n
Ca Al2 O3 -2_565 1_555 115.13(10) n
Ca Al2 O3 -2_565 -1_655 64.87(10) n
Ca Al2 O1 -2_665 1_555 127.02(14) n
Ca Al2 O1 -2_665 -1_655 52.98(14) n
Ca Al2 O2 -2_665 1_545 111.80(13) n
Ca Al2 O2 -2_665 -1_665 68.20(13) n
Ca Al2 O3 -2_665 1_555 135.45(9) n
Ca Al2 O3 -2_665 -1_655 44.55(9) n
O1 Al2 O1 1_555 -1_655 180.0 n
O1 Al2 O2 1_555 1_545 88.8(2) n
O1 Al2 O2 1_555 -1_665 91.2(2) n
O1 Al2 O3 1_555 1_555 90.34(12) n
O1 Al2 O3 1_555 -1_655 89.66(12) n
O1 Al2 O2 -1_655 1_545 91.2(2) n
O1 Al2 O2 -1_655 -1_665 88.8(2) n
O1 Al2 O3 -1_655 1_555 89.66(12) n
O1 Al2 O3 -1_655 -1_655 90.34(12) n
O2 Al2 O2 1_545 -1_665 180.0 n
O2 Al2 O3 1_545 1_555 89.52(14) n
O2 Al2 O3 1_545 -1_655 90.48(14) n
O2 Al2 O3 -1_665 1_555 90.48(14) n
O2 Al2 O3 -1_665 -1_655 89.52(14) n
O3 Al2 O3 1_555 -1_655 180.0 n
Ca Nb2 Ca 1_545 2_545 72.81(4) n
Ca Nb2 Ca 1_545 2_645 71.53(4) n
Ca Nb2 Ca 1_545 -1_665 179.9802 n
Ca Nb2 Ca 1_545 -2_565 108.47(4) n
Ca Nb2 Ca 1_545 -2_665 107.19(4) n
Ca Nb2 O1 1_545 1_555 124.23(13) n
Ca Nb2 O1 1_545 -1_655 55.77(13) n
Ca Nb2 O2 1_545 1_545 56.61(14) n
Ca Nb2 O2 1_545 -1_665 123.39(14) n
Ca Nb2 O3 1_545 1_555 52.09(9) n
Ca Nb2 O3 1_545 -1_655 127.91(9) n
Ca Nb2 Ca 2_545 2_645 108.78(17) n
Ca Nb2 Ca 2_545 -1_665 107.19(4) n
Ca Nb2 Ca 2_545 -2_565 71.22(17) n
Ca Nb2 Ca 2_545 -2_665 180.0 n
Ca Nb2 O1 2_545 1_555 52.98(14) n
Ca Nb2 O1 2_545 -1_655 127.02(14) n
Ca Nb2 O2 2_545 1_545 68.20(13) n
Ca Nb2 O2 2_545 -1_665 111.80(13) n
Ca Nb2 O3 2_545 1_555 44.55(9) n
Ca Nb2 O3 2_545 -1_655 135.45(9) n
Ca Nb2 Ca 2_645 -1_665 108.47(4) n
Ca Nb2 Ca 2_645 -2_565 179.972 n
Ca Nb2 Ca 2_645 -2_665 71.22(17) n
Ca Nb2 O1 2_645 1_555 133.61(13) n
Ca Nb2 O1 2_645 -1_655 46.39(13) n
Ca Nb2 O2 2_645 1_545 126.87(13) n
Ca Nb2 O2 2_645 -1_665 53.13(13) n
Ca Nb2 O3 2_645 1_555 64.87(10) n
Ca Nb2 O3 2_645 -1_655 115.13(10) n
Ca Nb2 Ca -1_665 -2_565 71.53(4) n
Ca Nb2 Ca -1_665 -2_665 72.81(4) n
Ca Nb2 O1 -1_665 1_555 55.77(13) n
Ca Nb2 O1 -1_665 -1_655 124.23(13) n
Ca Nb2 O2 -1_665 1_545 123.39(14) n
Ca Nb2 O2 -1_665 -1_665 56.61(14) n
Ca Nb2 O3 -1_665 1_555 127.91(9) n
Ca Nb2 O3 -1_665 -1_655 52.09(9) n
Ca Nb2 Ca -2_565 -2_665 108.78(17) n
Ca Nb2 O1 -2_565 1_555 46.39(13) n
Ca Nb2 O1 -2_565 -1_655 133.61(13) n
Ca Nb2 O2 -2_565 1_545 53.13(13) n
Ca Nb2 O2 -2_565 -1_665 126.87(13) n
Ca Nb2 O3 -2_565 1_555 115.13(10) n
Ca Nb2 O3 -2_565 -1_655 64.87(10) n
Ca Nb2 O1 -2_665 1_555 127.02(14) n
Ca Nb2 O1 -2_665 -1_655 52.98(14) n
Ca Nb2 O2 -2_665 1_545 111.80(13) n
Ca Nb2 O2 -2_665 -1_665 68.20(13) n
Ca Nb2 O3 -2_665 1_555 135.45(9) n
Ca Nb2 O3 -2_665 -1_655 44.55(9) n
O1 Nb2 O1 1_555 -1_655 180.0 n
O1 Nb2 O2 1_555 1_545 88.8(2) n
O1 Nb2 O2 1_555 -1_665 91.2(2) n
O1 Nb2 O3 1_555 1_555 90.34(12) n
O1 Nb2 O3 1_555 -1_655 89.66(12) n
O1 Nb2 O2 -1_655 1_545 91.2(2) n
O1 Nb2 O2 -1_655 -1_665 88.8(2) n
O1 Nb2 O3 -1_655 1_555 89.66(12) n
O1 Nb2 O3 -1_655 -1_655 90.34(12) n
O2 Nb2 O2 1_545 -1_665 180.0 n
O2 Nb2 O3 1_545 1_555 89.52(14) n
O2 Nb2 O3 1_545 -1_655 90.48(14) n
O2 Nb2 O3 -1_665 1_555 90.48(14) n
O2 Nb2 O3 -1_665 -1_655 89.52(14) n
O3 Nb2 O3 1_555 -1_655 180.0 n
Ca O1 Ca 2_545 -1_665 163.6(3) n
Ca O1 Ca 2_545 -2_565 99.1(2) n
Ca O1 Al1 2_545 1_555 86.38(13) n
Ca O1 Nb1 2_545 1_555 86.38(13) n
Ca O1 Al2 2_545 1_555 90.79(16) n
Ca O1 Nb2 2_545 1_555 90.79(16) n
Ca O1 Ca -1_665 -2_565 97.26(15) n
Ca O1 Al1 -1_665 1_555 90.40(15) n
Ca O1 Nb1 -1_665 1_555 90.40(15) n
Ca O1 Al2 -1_665 1_555 85.93(11) n
Ca O1 Nb2 -1_665 1_555 85.93(11) n
Ca O1 Al1 -2_565 1_555 105.81(16) n
Ca O1 Nb1 -2_565 1_555 105.81(16) n
Ca O1 Al2 -2_565 1_555 97.06(16) n
Ca O1 Nb2 -2_565 1_555 97.06(16) n
Al1 O1 Al2 1_555 1_555 157.1(2) n
Al1 O1 Nb2 1_555 1_555 157.1(2) n
Nb1 O1 Al2 1_555 1_555 157.1(2) n
Nb1 O1 Nb2 1_555 1_555 157.1(2) n
Ca O2 Ca 1_555 -1_665 97.7(2) n
Ca O2 Ca 1_555 -2_575 164.9(3) n
Ca O2 Al1 1_555 1_555 91.51(17) n
Ca O2 Nb1 1_555 1_555 91.51(17) n
Ca O2 Al2 1_555 1_565 85.28(13) n
Ca O2 Nb2 1_555 1_565 85.28(13) n
Ca O2 Ca -1_665 -2_575 97.37(15) n
Ca O2 Al1 -1_665 1_555 97.81(17) n
Ca O2 Nb1 -1_665 1_555 97.81(17) n
Ca O2 Al2 -1_665 1_565 104.09(16) n
Ca O2 Nb2 -1_665 1_565 104.09(16) n
Ca O2 Al1 -2_575 1_555 87.37(13) n
Ca O2 Nb1 -2_575 1_555 87.37(13) n
Ca O2 Al2 -2_575 1_565 90.14(16) n
Ca O2 Nb2 -2_575 1_565 90.14(16) n
Al1 O2 Al2 1_555 1_565 158.1(3) n
Al1 O2 Nb2 1_555 1_565 158.1(3) n
Nb1 O2 Al2 1_555 1_565 158.1(3) n
Nb1 O2 Nb2 1_555 1_565 158.1(3) n
Ca O3 Ca 1_545 2_545 104.74(7) n
Ca O3 Al1 1_545 2_545 91.17(18) n
Ca O3 Nb1 1_545 2_545 91.17(18) n
Ca O3 Al2 1_545 1_555 89.64(18) n
Ca O3 Nb2 1_545 1_555 89.64(18) n
Ca O3 Al1 2_545 2_545 100.8(2) n
Ca O3 Nb1 2_545 2_545 100.8(2) n
Ca O3 Al2 2_545 1_555 100.0(2) n
Ca O3 Nb2 2_545 1_555 100.0(2) n
Al1 O3 Al2 2_545 1_555 158.27(7) n
Al1 O3 Nb2 2_545 1_555 158.27(7) n
Nb1 O3 Al2 2_545 1_555 158.27(7) n
Nb1 O3 Nb2 2_545 1_555 158.27(7) n
loop_
_geom_bond_atom_site_label_1
_geom_bond_atom_site_label_2
_geom_bond_site_symmetry_2
_geom_bond_distance
_geom_bond_publ_flag
Ca Ca 2_545 3.861(3) n
Ca Ca 2_555 3.861(3) n
Ca Ca 2_645 3.772(3) n
Ca Ca 2_655 3.772(3) n
Ca Ca -1_665 3.805(12) n
Ca Ca -1_666 3.851(12) n
Ca Al1 1_555 3.320(4) n
Ca Al1 1_655 3.267(4) n
Ca Al1 2_545 3.456(3) n
Ca Al1 2_555 3.183(4) n
Ca Nb1 1_555 3.320(4) n
Ca Nb1 1_655 3.267(4) n
Ca Nb1 2_545 3.456(3) n
Ca Nb1 2_555 3.183(4) n
Ca Al2 1_555 3.444(4) n
Ca Al2 1_565 3.169(4) n
Ca Al2 2_555 3.332(4) n
Ca Al2 2_655 3.282(4) n
Ca Nb2 1_555 3.444(4) n
Ca Nb2 1_565 3.169(4) n
Ca Nb2 2_555 3.332(4) n
Ca Nb2 2_655 3.282(4) n
Ca O1 1_555 3.178(6) n
Ca O1 2_555 2.660(7) n
Ca O1 -1_665 2.627(6) n
Ca O1 -2_666 2.395(6) n
Ca O2 1_555 2.655(7) n
Ca O2 2_545 3.177(6) n
Ca O2 -1_665 2.392(6) n
Ca O2 -2_676 2.626(6) n
Ca O3 1_555 2.9718(14) n
Ca O3 1_565 2.5006(15) n
Ca O3 2_555 2.373(2) n
Ca O3 2_655 3.025(2) n
Al1 Ca 1_455 3.267(4) n
Al1 Ca 1_555 3.320(4) n
Al1 Ca 2_545 3.183(4) n
Al1 Ca 2_555 3.456(3) n
Al1 Ca -1_565 3.320(4) n
Al1 Ca -1_665 3.267(4) n
Al1 Ca -2_565 3.456(3) n
Al1 Ca -2_575 3.183(4) n
Al1 O1 1_555 1.924(3) n
Al1 O1 -1_565 1.924(3) n
Al1 O2 1_555 1.924(3) n
Al1 O2 -1_565 1.924(3) n
Al1 O3 2_555 1.919(5) n
Al1 O3 -2_565 1.919(5) n
Nb1 Ca 1_455 3.267(4) n
Nb1 Ca 1_555 3.320(4) n
Nb1 Ca 2_545 3.183(4) n
Nb1 Ca 2_555 3.456(3) n
Nb1 Ca -1_565 3.320(4) n
Nb1 Ca -1_665 3.267(4) n
Nb1 Ca -2_565 3.456(3) n
Nb1 Ca -2_575 3.183(4) n
Nb1 O1 1_555 1.924(3) n
Nb1 O1 -1_565 1.924(3) n
Nb1 O2 1_555 1.924(3) n
Nb1 O2 -1_565 1.924(3) n
Nb1 O3 2_555 1.919(5) n
Nb1 O3 -2_565 1.919(5) n
Al2 Ca 1_545 3.169(4) n
Al2 Ca 1_555 3.444(4) n
Al2 Ca 2_545 3.332(4) n
Al2 Ca 2_645 3.282(4) n
Al2 Ca -1_655 3.444(4) n
Al2 Ca -1_665 3.169(4) n
Al2 Ca -2_565 3.282(4) n
Al2 Ca -2_665 3.332(4) n
Al2 O1 1_555 1.969(3) n
Al2 O1 -1_655 1.969(3) n
Al2 O2 1_545 1.963(3) n
Al2 O2 -1_665 1.963(3) n
Al2 O3 1_555 1.963(5) n
Al2 O3 -1_655 1.963(5) n
Nb2 Ca 1_545 3.169(4) n
Nb2 Ca 1_555 3.444(4) n
Nb2 Ca 2_545 3.332(4) n
Nb2 Ca 2_645 3.282(4) n
Nb2 Ca -1_655 3.444(4) n
Nb2 Ca -1_665 3.169(4) n
Nb2 Ca -2_565 3.282(4) n
Nb2 Ca -2_665 3.332(4) n
Nb2 O1 1_555 1.969(3) n
Nb2 O1 -1_655 1.969(3) n
Nb2 O2 1_545 1.963(3) n
Nb2 O2 -1_665 1.963(3) n
Nb2 O3 1_555 1.963(5) n
Nb2 O3 -1_655 1.963(5) n
O1 Ca 1_555 3.178(6) n
O1 Ca 2_545 2.660(7) n
O1 Ca -1_665 2.627(6) n
O1 Ca -2_565 2.395(6) n
O1 Al1 1_555 1.924(3) n
O1 Nb1 1_555 1.924(3) n
O1 Al2 1_555 1.969(3) n
O1 Nb2 1_555 1.969(3) n
O2 Ca 1_555 2.655(7) n
O2 Ca 2_555 3.177(6) n
O2 Ca -1_665 2.392(6) n
O2 Ca -2_575 2.626(6) n
O2 Al1 1_555 1.924(3) n
O2 Nb1 1_555 1.924(3) n
O2 Al2 1_565 1.963(3) n
O2 Nb2 1_565 1.963(3) n
O3 Ca 1_545 2.5006(15) n
O3 Ca 1_555 2.9718(14) n
O3 Ca 2_545 2.373(2) n
O3 Ca 2_645 3.025(2) n
O3 Al1 2_545 1.919(5) n
O3 Nb1 2_545 1.919(5) n
O3 Al2 1_555 1.963(5) n
O3 Nb2 1_555 1.963(5) n